Barrier Solutions - Info Page 3

GENERAL

1.01 SCOPE OF WORK

Furnish flexible membrane lining as shown on the submitted drawings. All work shall be done in strict accordance with the project drawings, these specifications and the membrane fabricator's approved shop drawings.

Geomembrane panels will be supplied sufficient to cover all areas, including appurtenances, as required in the project and shown on the drawings. The fabricator shall allow for shrinkage and wrinkling of the field panels.

1.02 PRODUCTS

35 GAUGE PVC GEOMEMBRANE LINER, FISH GRADE

MATERIAL: Geomembrane grade PVC sheeting,

DESCRIPTION: The material is a specially formulated PVC sheeting. All ingredients are first quality materials, compounded and manufactured into sheeting according to the best practices of the industry.

REFERENCE: 56030, 56031, 56066, 56093, 59996, 59997

PURPOSE: This product bulletin describes sheeting designed for containment linings in aquaculture applications. Use of this material must be in compliance with recommended application guidelines.

PHYSICAL PROPERTIES TEST METHOD TYPICAL PROPERTIES

Thickness (in.) 0.035

Tensile strength (psi) ASTM D882 MD 2500 TD 2300

100% Modulus (psi) ASTM D882 MD 1100 TD 1000

Elongation at break (%) ASTM D882 MD 350 TD 350

Tear resistance (gm./mil) ASTM D1004 MD 127 TD 140

Low temp. impact(-200F) ASTM Dl 790 MD PASS

Water extraction (%) ASTM D3083 –0.03 7 days

Dimensional stability(%) ASTM D1204 30 min. 1000C MD -3.5 TD +1.0

MEMBRANE LINER, POLYVINYL CHLORIDE (PVC), REGULAR

Property Test Method Specified Values

Thickness mils ASTMD 1593 20       30      40      50       60

Specific Gravity, min. AST D 792 1.23      1.23   1.23   1.23    1.23

Tensile Strength, psi, min.
(Breaking Factor, lb./in. width min.) ASTM D 882 2300    2300   2300 2300   2300
    46        69       92    115     138

Elongation, at break, % mm. ASTM D 882 325      350     400    450     450

Modulus at 100% Elongation, psi, (Lb./in. width mm.) ASTM D 882 1000    1000    1000 1000 1000

Tear Resistance, lb./in., mm.
(Lb.., mm.) ASTM D 1004300 (6.0)   (9.0)   (12.0) (15.0) (15.0)

Low Temperature, Deg. F ASTM D 1790    -15    –20     –25      –30     -30

Dimensional Stability
% change, max. ASTM D 1204 (212 deg. F, 15 min.)     3.5     3.5     3.5      3.5      3.5

Water Extraction, % loss, max. ASTM D 3083 0.35    0.35   0.35    0.35   0.35

Volatility, % loss, max. ASTM D 1203 0.90    0.70   0.50    0.50   0.50

Hydrostatic Resistance, psi, mm. ASTM D 721      60       85    110     150   175

PHYSICAL PROPERTIES	TEST METHOD	TYPICAL PROPERTIES
Thickness (in.)		0.035
Tensile strength (psi)	ASTM D882	MD 2500 TD 2300
100% Modulus (psi)	ASTM D882	MD 1100 TD 1000
Elongation at break (%)	ASTM D882	MD 350 TD 350
Tear resistance (gm./mil)	ASTM D1004	MD 127 TD 140
Low temp. impact(-200F)	ASTM Dl 790	MD PASS
Water extraction (%)	ASTM D3083	–0.03 7 days
Dimensional stability(%)	ASTM D1204 30 min. 1000C	MD -3.5 TD +1.0

Property	Test Method	Specified Values
Thickness mils	ASTMD 1593	20 30 40 50 60
Specific Gravity, min.	AST D 792	1.23 1.23 1.23 1.23 1.23
Tensile Strength, psi, min. (Breaking Factor, lb./in. width min.)	ASTM D 882	2300 2300 2300 2300 2300 46 69 92 115 138
Elongation, at break, % mm.	ASTM D 882	325 350 400 450 450
Modulus at 100% Elongation, psi, (Lb./in. width mm.)	ASTM D 882	1000 1000 1000 1000 1000
Tear Resistance, lb./in., mm. (Lb.., mm.)	ASTM D 1004300	(6.0) (9.0) (12.0) (15.0) (15.0)
Low Temperature, Deg. F	ASTM D 1790	-15 –20 –25 –30 -30
Dimensional Stability % change, max.	ASTM D 1204 (212 deg. F, 15 min.)	3.5 3.5 3.5 3.5 3.5
Water Extraction, % loss, max.	ASTM D 3083	0.35 0.35 0.35 0.35 0.35
Volatility, % loss, max.	ASTM D 1203	0.90 0.70 0.50 0.50 0.50
Hydrostatic Resistance, psi, mm.	ASTM D 721	60 85 110 150 175